This paper newly proposes dynamic failure criteria for laser welds to describe strain-rate dependent failure behavior of laser welds in crash analysis of an auto-body. The failure criteria had been deduced from experimental results with nine different loading conditions including the normal loading and the pure-shear loading condition. Quasi-static and dynamic failure tests for 25 mm stitch-type laser welds of SPRC340 1.2t and SPCC 1.0t, 20 mm stitch-type laser welds of CR340 1.2t and f 8 mm O-type laser welds of SPRC340 1.2t were examined in this paper. A universal testing machine of INSTRON 5583 was used in the quasi-static failure tests and a high speed material testing machine was utilized in the dynamic failure tests at the intermediate strain rates of 1/sec, 10/sec and 100/sec, as the strain rate most relevant to an automotive crash event lies in the intermediate strain rate range. In order to obtain the failure load under the combined normal and shear loading condition including a pure-shear failure loading condition, the testing systems were newly designed and prepared. The prepared apparatus guarantees prevention of unfavorable rotation of the bead using guide plates during failure tests under the combined loading condition. A new testing fixture and a specimen were designed to evaluate the pure-shear strength of laser welds fabricated using the same welding condition with a two-layered lap joint. With the aid of the proposed testing fixtures and specimens, the normal and the shear failure loads of laser welds could be acquired accurately by simple trigonometric functions of the applied failure load and the initial loading angle.

Failure loads and failure behavior of laser welds were evaluated using the experimental results. In the failure tests of the stitch-type laser welds and the O-type laser welds, two types of failure modes were observed: base metal failure took place from 0° to about 60°; and interfacial failure took place at the mid plane of a bead from 80° to 90°. There is a transition region between the angle of 75° and 80° where the failure mode of laser welds changes from base metal failure to interfacial failure. From the failure loads measured in the dynamic failure tests, the strain-rate dependent failure contour of laser welds were constructed by decomposing the failure loads at various loading angles into the two components along the normal and shear directions and decomposed ones were plotted in the force domain. It was found that the failure contour of the laser welds expands with increasing strain rates.

Based on the experimental data, a new failure criterion was proposed for prediction of failure behavior of laser welds. In the case of the base metal failure, the shear failure load increases as the normal failure load decrease with increase of the loading angle. The base metal failure contour shows a near-elliptical contour in terms of the normal and shear loads. Therefore, the failure of laser welds can be predicted by a similar failure criterion to that for spot welds. The transition point is observed around a loading angle of 75° due to the change in the failure mode from base metal failure to interfacial failure. In the case of the interfacial failure, the shear failure load decreases as the normal failure load decrease with increase of the loading angle. Consequently, the new criterion introduces to describe the interfacial failure other than the failure criterion for the base metal failure. In this paper, the dynamic failure criterion is divided into two regions of a base metal failure and an interfacial failure. The dynamic failure criterion for the base metal failure region is expressed as a function of the normal and the virtual shear load, which is the so-called b-norm function, while the dynamic failure criterion for the interfacial failure region is explained in a form of a modified power law function. The dynamic failure criterion for the base metal failure region is verified based on the assumption of a stress field around a bead with the aid of finite element analysis which is induced by the normal and the shear loads. The strain-rate sensitivity values of the normal and the virtual shear failure load are assigned as an exponential function of the logarithm of the strain rate. The dynamic failure criterion for the interfacial failure criterion is proposed to describe the failure contour in the interfacial failure region which is represented empirically. The strain-rate sensitivity value of the corresponding shear failure load for the normal load acting on laser welds is assigned as an exponential function of the logarithm of the strain rate and the change of shear failure load hardening due to the change of strain rate is considered. The maximum value of the failure criteria is obtained after calculating the base metal failure criterion and the interfacial failure criterion with the normal load and the shear load acting on laser welds. The failure mode and the failure of laser welds are determined when the maximum value reaches to 1. The failure criterion newly proposed provides a fairly accurate prediction of the failure load obtained from the experiments under combined normal and shear loading conditions.

A modified dynamic failure criterion was proposed to express the proposed failure criteria separated into two portions with a single function. It is possible to describe the failure contour as one function simply by translating the b-norm function toward the normal load axis direction and the shear load axis direction. There are five coefficients which are obtained from interpolation result for the failure contours of laser welds. The strain-rate sensitivity values of each coefficient are assigned as an exponential function of the logarithm of the strain rate. The modified dynamic failure criterion describes the failure contour of stitch-type laser welds simply and accurately. There are very few differences between the newly proposed dynamic failure criterion and the modified dynamic failure criterion to describe the failure contour of stitch-type laser welds. However, there are large differences between the proposed failure criterion and the modified failure criterion to describe the failure contour of O-type laser welds at the transition point. The modified failure criterion can describe the experimental results accurately like stitch-type laser welds when the failure loads change gradually at the transition point of a failure mode. However, the modified failure criterion cannot describe the failure contour of O-type laser welds when the failure loads change sharply around the transition point of a failure mode. Therefore, the newly proposed dynamic failure criterion is better than the modified failure criterion to describe the failure contour of laser welds.
번호 제목 저자명 날짜 조회 수
27 Anisotropic Fracture Limit for the Failure Prediction of Advanced High-Strength Steel Sheets (고강도 강판의 파괴 예측을 위한 이방성 파괴 한계에 관한 연구) 박남수  2017.06.07 206
26 A Study on the Nonlinear Behaviors of Polymer-Bonded Explosives Considering Stress Softening Effect(응력연화현상을 고려한 복합화약의 비선형 거동에 관한 연구) 염기선  2013.09.08 4792
25 Rate-Dependent Hardening Model for Polymer-Bonded Explosives Considering a Wide Range of Strain Rates (광범위한 변형률속도를 고려한 복합화약의 변형률속도 의존 경화모델) 박충희  2013.08.30 3582
» Dynamic Failure Criteria of a Laser-welded Region under Combined Loading Conditions for Auto-body Crash Analyses (차체용 부재의 충돌해석을 위한 복합하중조건에서 레이저 용접부의 동적 파단조건 연구) 하지웅  2013.04.14 7312
23 Rate Dependent Hardening Model for Pure Titanium Considering the Effect of Deformation Twinning (쌍정의 영향을 고려한 티타늄의 변형률속도 의존 경화 모델) 안광현  2012.12.12 17015
22 Strain-Rate Dependent Anisotropic Yield Criteria for Auto-body Steel Sheets (자동차용 강판의 변형률속도 의존 이방성 항복함수에 관한 연구) 허지향  2012.12.11 17879
21 A New Ductile Fracture Criterion for the Formability Prediction of Steel Sheets and Its Application to Finite Element Analysis (강판의 성형성 예측을 위한 새로운 연성 파괴 조건 및 유한 요소 해석에의 응용) [1] Yanshan Lou  2012.12.10 20882
20 Measurement Uncertainty Evaluation for High Strain Rate Tensile Properties of Auto-body Steel Sheet (자동차용 강판 고속인장물성 데이터의 측정불확도 산출) 정세환  2012.12.10 17630
19 A Study on a Continuum Damage Yield Function to Predict Ductile Fracture of Materials (재료의 연성파단을 예측하기 위한 연속체 손상 항복 함수에 관한 연구) 고윤기  2012.12.10 14492
18 A Study on the Tension/Compression Hardening Behavior of Auto-body Steel Sheets Considering the Pre-strain and the Strain Rate (초기 변형률 및 변형률 속도를 고려한 차체 강판의 인장/압축 경화 거동에 관한 연구) [1] 배기현  2011.01.11 20195
17 Forming Limit Diagram of Auto-body Steel Sheets at High Strain Rates for Sheet Metal Forming and Crashworthiness (박판성형 및 충돌성능 향상을 위한 고변형률속도에서의 차체강판 성형한계도) 김석봉  2010.07.13 21490
16 Evaluation of a cast-joining process of dual metal crankshafts for heavy-duty engines with ductile cast iron and high strength forged steel(구상흑연주철과 고강도 단조강의 주조접합 이종금속을 이용한 중대형 엔진 크랭크샤프트의 평가) 한 신  2010.07.13 17752
15 A Study on Material Properties of OFHC Copper Film at High Strain Rates using High-Speed Micro Material Testing Machine (고속마이크로재료시험기를 이용한 무산소동 박판의 고변형률속도 재료물성치 연구) 김진성  2010.07.13 20066
14 Microscopic investigation of the strain rate hardening for auto-body steel sheet(차체강판 변형률속도 경화의 미시적 관찰) 윤종헌  2010.07.13 16794
13 Analysis of Elasto-Plastic Stress Waves by a Time Discontinuous Variational Integrator of Hamiltonian with a Second-Order Integration Scheme of the Constitutive Model (해밀토니안의 시간 불연속 변분적분기와 구성방정식의 2차 정확도 적분법을 이용한 탄소 조상순  2008.12.15 21560
12 A Study on the Dynamic Failure Model of a Spot Weld under Combined Loading Conditions for Auto-body Crash Analyses (차체용 부재의 충돌해석을 위한 복합하중조건에서 점용접부의 동적 파단모델 연구) [1] 송정한  2008.07.24 18427
11 Study on Dynamic Tensile Tests of Auto-body Steel Sheet at the Intermediate Strain Rate for Material Constitutive Equations (차체강판의 중변형률 속도에서의 동적 인장시험 및 물성 구성방정식에 관한 연구) 임지호  2005.11.29 25333
10 Dynamic Formulation of Finite Element Limit Analysis for Impact Simulation of Structural Members (구조부재의 충돌해석을 위한 유한요소 극한해석의 동적 수식화) 김기풍  2005.11.29 17645
9 Finite Element Inverse Approach and Initial Guess Generation for Sheet Metal Forming Analysis of Complicated Auto-body Members (복잡한 차체부재의 박판성형공정을 위한 유한요소 역해석 및 초기추측치 계산) 김승호  2005.11.29 18964
8 Development of a Nonlinear Degenerated Shell Element with the Drilling Degree of Freedom by the Cubic Polynomial Interpolation and the Assumed Strain Method (드릴링 자유도의 삼차 근사법과 대체변형률법을 이용한 비선형 감절점 쉘 요소의 개발) 이형욱  2005.11.29 17573